Item | RSB200 | RSB300 | RSB350 | RSY150 | RSY250 | RSY300 | RSY350 |
Tensile strength MPa≥ | 5 | 7 | 11 | 8 | 10 | 12 | 15 |
Aging Coefficient ≥ | 0.9 |
|
|
|
|
|
|
Density g/cm³ g/cm3 | 1.6 2.0 | 1.6 1.8 |
|
|
| ||
Compressibility % | 12 ± 7 |
|
|
|
|
|
|
Rebound degree | 35 | 40 | 45 | 40 | 45 | 50 | 50 |
Pliability | No Crack |
|
|
|
|
|
|
Stress-relaxation≤ % | 45 | 45 | 45 | 40 | 40 | 30 | 30 |
Oil sealing |
|
|
| 10 MPa pressure for 30 min | 12 MPa pressure for 30 min | 15MPa pressure for 30 min | 16 MPa pressure for 30 min |
With the temperature | No leaking | No leaking | No leaking | No leaking | |||
of 15to 30,.75aviation gasoline for 30 min |
| 12 Mpa | 15MPa | 16 MPa | |||
With the temperature of 150±2,dipped in No.20 aviation oil for 5h,then taken out and laid for 5min. | Tensile strength-reducing % | 40 | 30 | 25 | 25 | ||
Thickness-increasing %≤ | 520 | 520 | 518 | 518 | |||
Appearance change | No bubble |
|
|
| |||
With the temperature | Tensile strength MPa ≥ | 5 | 6 | 8 | 10 | ||
of 15 to 30 ,dipped in No.75 aviation oil for 5h,then taken out and laid for 5min. | Thickness-increasing % | 525 | 525 | 520 | 520 | ||
| Pliability | No Crack |
|
|
|